Reference type: Journal
Authors: Hicks JC, Dabestani R, Buchanan AC, Jones CW
Article Title: Spacing and Site Isolation of Amine Groups in 3-Aminopropyl-Grafted Silica Materials: The Role of Protecting Groups.
Publication date: 2006
Journal: Chemistry of Materials
Volume: 18
Issue: (21)
Page numbers: 5022-5032.
DOI: 10.1021/cm061382w

Abstract: The relative spacing of amines in 3-aminopropylsilyl-grafted silica is studied by solid-state fluorescence spectroscopy of 1-pyrenecarboxylic acid (PCA) and 1-pyrenebutyric acid (PBA) bound to traditionally prepared, deprotected benzyl- or deprotected trityl-spaced aminosilicas. Thermogravimetric analysis and FT-Raman spectroscopy results show evidence that the protected imine can be cleaved to yield the corresponding amine in essentially quantitative yield. The steady-state fluorescence spectroscopic data of either PCA or PBA indicate that the number of amine pairs on the surface separated by a distance of 1 nm or less decreases as the total amine loading decreases. Both the intensity ratio of the excimer band to the monomer band (I470/I384 or Iexc/Imon) and lifetime decay studies of the fluorophore are useful probes of the amine spacing. Separation of amines on the surface can be achieved by either use of a protected synthesis route or through reduction of the concentration of the unprotected 3-aminopropyltrimethoxysilane used in the grafting solution. However, the two routes lead to materials with significantly different average amine spacings. Due to clustering of unprotected amines in solution before grafting or on the surface during the grafting process, amine-amine distances on the surface of materials prepared by an unprotected synthesis are on average smaller than when a protected synthesis is used. With the protected synthesis, evidence suggests that the amines are more isolated, with larger average amine-amine distances when compared to corresponding materials with a similar amine loading prepared via an unprotected synthesis. This is attributed to both the steric influence of the protecting groups and a reduction in silane clustering in solution due to protection of the amines before grafting. Thus, the mechanism of surface amine spacing when using the protection-deprotection strategy appears to involve both of these factors (especially in the case of trityl-spaced samples).

Featured products

 

atrazine template mug ball and stick model

 

multi MIPs logo beer stein

 

mips logo apron